A Review on Repair Techniques for Crack in Metals

Shubhaseesh Srivastava

Abstract


Cracks are fractures that form on the surface or beneath the surface of a substance. Crack initiation and growth may be persuaded by propagation energy expected from mechanical, thermal, chemical, and metallurgical causes, or a combination of these. Cooling, crater, grinding, pickling, solidification, centreline, heat treatment, machining tears, plating, stress corrosion, fatigue, creep, and hydrogen cracks are some of the several forms of metal cracks. Cracks can expand and lead to a complete fracture of the component, posing a serious threat to the component's life and perhaps resulting in serious injury or death. Metals can brittle fracture with little or no obvious warning. The discovery of any fractures necessitates prompt action to stop the cracks from spread-out to the point of fracture. Through study, a few fractures detection and repair methods in metals have been created, characterized, and confirmed. The strategies for repairing metal cracks are discussed in this study

Keywords


Crack, Fracture damage, Microcracks, Laser Additive Technology, Stitching.

Full Text:

PDF

References


Kelbassa, A.P. Patrick, J. Dietrich and J. Wilkes, “Manufacture and repair of aero engine

components using laser technology (invited paper),” in 3rd Pacific International Conference on

Application of Lasers and Optics, Germany, 2008.

J. Yu, M. Rombouts, G. Maes and F. Motmans, “Material properties of Ti6Al4V parts produced

by laser metal deposition,” Physics Procedia, vol. 39, pp. 416–424, 2012.

S.J. Ahn and P.K. Basu, “Locally refined p-FEM modeling of patch repaired plates,” Journal of

Composite Structures, vol. 93, pp. 1704–1716, 2011.

V. Sabelkin, V.S. Mall and J.B. Avram, “Fatigue crack growth analysis of stiffened cracked panel

repaired with bonded composite patch,” Engineering Fracture Mechanics, vol. 73, pp. 1553–1567,

R. Srilakshmi, M. Ramji and V. Chinthapenta, “Fatigue crack growth study of CFRP patch

repaired Al 2014-T6 panel having an inclined center crack using FEA and DIC,” Journal of

Engineering Fracture Mechanics, vol. 134, pp. 182–201, 2015.

D. Seo and J. Lee, “Fatigue crack growth behavior of cracked aluminum plate repaired with

composite patch,” Journal of Composite Structures, vol. 57, pp. 323–330, 2002.

B. Graf, A. Gumenyuka and M. Rethmeiera, “Laser metal deposition as repair technology for

stainless steel and titanium alloys,” Physics Procedia 39, vol. 39, pp. 376–381, 2012.

S.M.A. Khan, F. Benyahia and B.B.A.A. Bouiadjra, “Analysis and Repair of Crack Growth

Emanating from V-Notch under Stepped Variable Fatigue Loading,” XVII International

Colloquium on Mechanical Fatigue of Metals (ICMFM17), vol. 74, pp. 151–156, 2014.

M.R. Ayatollahi, S.M.J. Razavi and H.R. Chamani, “Fatigue life extension by crack repair using

stop-hole technique under pure mode-I and pure mode-II loading conditions,” XVII International

Colloquium on Mechanical Fatigue of Metals (ICMFM17), vol. 74, pp. 18–21, 2014.

R. Emdad and R. Al-Mahaidi, “Effect of prestressed CFRP patches on crack growth of centrenotched steel plates,” Journal of Composite Structures, vol. 123, pp. 109–122, 2015.

J.W. Murray and A.T. Clare, “Repair of EDM induced surface cracks by pulsed electron beam

irradiation,” Journal of Materials Processing Technology, vol. 212, pp. 2642–2651, 2012.

R. Dexter, K. Anami, P. Albrecht, B. Brakke, O. Bucak, R. Connor, G. Decorges and J. Fisher,

“Manual for Repair and Retrofit of Fatigue Cracks in Steel Bridges,” U.S Department of

Transportation Federal Highway Administration (FHWA), New York, 2013.


Refbacks

  • There are currently no refbacks.